摘要:<p style="margin:0pt;"> <span style="font-family:宋體;font-size:10.5pt;mso-spacerun:&quot;yes&quot;;mso-ascii-font-family:Calibri;mso-hansi-font-family:Calibri;mso-bidi-font-family:&quot;Times New Roman&quot;;mso-font-kerning:1.0000pt;"><span style="font-family:宋體;">西安</span></span><span style="font-family:宋體;font-size:10.5pt;mso-spacerun:&quot;yes&quot;;mso-ascii-font-family:Calibri;mso-hansi-font-family:Calibri;mso-bidi-font-family:&quot;Times New Roman&quot;;mso-font-kerning:1.0000pt;"><span style="font-family:宋體;">不鏽鋼板材拉深過程中開裂原因</span></span> </p> <p style="margin:0pt;"> <span style="font-family:宋體;font-size:10.5pt;mso-spacerun:&quot;yes&quot;;mso-ascii-font-family:Calibri;mso-hansi-font-family:Calibri;mso-bidi-font-family:&quot;Times New Roman&quot;;mso-font-kerning:1.0000pt;"><span style="font-family:宋體;">拉伸奧氏體不鏽鋼板材有時會出現開裂現象,而且每個現象不太一樣。</span></span> </p> <p style="margin:0pt;"> <span style="font-family:宋體;font-size:10.5pt;mso-spacerun:&quot;yes&quot;;mso-ascii-font-family:Calibri;mso-hansi-font-family:Calibri;mso-bidi-font-family:&quot;Times New Roman&quot;;mso-font-kerning:1.0000pt;"><span style="font-family:宋體;">有的是拉伸變形之後開裂;有的是從凹模內退出時就立馬開裂;有的是拉伸變形之後受到撞擊或振動時開裂;也有的是拉伸變形過後存放一段時間或使用過程中突然開裂。</span></span> </p> <p style="margin:0pt;"> <span style="font-family:宋體;font-size:10.5pt;mso-spacerun:&quot;yes&quot;;mso-ascii-font-family:Calibri;mso-hansi-font-family:Calibri;mso-bidi-font-family:&quot;Times New Roman&quot;;mso-font-kerning:1.0000pt;"><span style="font-family:宋體;">其實開裂原因主要是因為奧氏體不鏽鋼板材的延展性比較低、彈性模量</span>E<span style="font-family:宋體;">有點大,硬化指數比較高,而且從屈服到開裂的塑性變形階段比較短。</span></span> </p> <p style="margin:0pt;"> <span style="font-family:宋體;font-size:10.5pt;mso-spacerun:&quot;yes&quot;;mso-ascii-font-family:Calibri;mso-hansi-font-family:Calibri;mso-bidi-font-family:&quot;Times New Roman&quot;;mso-font-kerning:1.0000pt;"><span style="font-family:宋體;">奧氏體不鏽鋼的冷作硬化指數相對比較高,而且是亞穩定型不鏽鋼,在變形時會發生相變,形成馬氏體組織。馬氏體相性比較脆,所以容易會開裂。在塑性變形時,隨著奧氏體相變形量的增大,誘發的馬氏體相含量也會隨著變形量的增大而增多,殘餘應力也就越高。從而形成惡性循環,在拉伸過程中奧氏體不鏽鋼板材也就越容易出現開裂現象。</span></span> </p> <p style="margin:0pt;"> <span style="font-family:宋體;font-size:10.5pt;mso-spacerun:&quot;yes&quot;;mso-ascii-font-family:Calibri;mso-hansi-font-family:Calibri;mso-bidi-font-family:&quot;Times New Roman&quot;;mso-font-kerning:1.0000pt;"><span style="font-family:宋體;">其實在奧氏體不鏽鋼板材的拉伸過程中還可以采取下列預防措施:</span></span> </p> <p style="margin:0pt;"> <span style="font-family:宋體;font-size:10.5pt;mso-spacerun:&quot;yes&quot;;mso-ascii-font-family:Calibri;mso-hansi-font-family:Calibri;mso-bidi-font-family:&quot;Times New Roman&quot;;mso-font-kerning:1.0000pt;"><span style="font-family:宋體;">可以在凹、凸模之間塗上潤滑劑,產生一層具備一定的韌性和延展性的薄膜,這對奧氏體不鏽鋼板材的拉伸效果明顯。</span></span> </p> <p style="margin:0pt;"> <span style="font-family:宋體;font-size:10.5pt;mso-spacerun:&quot;yes&quot;;mso-ascii-font-family:Calibri;mso-hansi-font-family:Calibri;mso-bidi-font-family:&quot;Times New Roman&quot;;mso-font-kerning:1.0000pt;"><span style="font-family:宋體;">可以采用白口鑄鐵作為壓邊圈磨具,錐形壓邊圈也可以使用,因為白口鑄鐵的存油性能比較好,極易產生潤滑油膜。</span></span> </p> <p style="margin:0pt;"> <span style="font-family:宋體;font-size:10.5pt;mso-spacerun:&quot;yes&quot;;mso-ascii-font-family:Calibri;mso-hansi-font-family:Calibri;mso-bidi-font-family:&quot;Times New Roman&quot;;mso-font-kerning:1.0000pt;"><span style="font-family:宋體;">把奧氏體不鏽鋼板材的邊緣加工光滑些,不能有微裂缺口,這樣有效避免開裂。</span></span> </p>

西安不鏽鋼板材拉深過程中開裂原因

拉伸奧氏體不鏽鋼板材有時會出現開裂現象,而且每個現象不太一樣。

有的是拉伸變形之後開裂;有的是從凹模內退出時就立馬開裂;有的是拉伸變形之後受到撞擊或振動時開裂;也有的是拉伸變形過後存放一段時間或使用過程中突然開裂。

其實開裂原因主要是因為奧氏體不鏽鋼板材的延展性比較低、彈性模量E有點大,硬化指數比較高,而且從屈服到開裂的塑性變形階段比較短。

奧氏體不鏽鋼的冷作硬化指數相對比較高,而且是亞穩定型不鏽鋼,在變形時會發生相變,形成馬氏體組織。馬氏體相性比較脆,所以容易會開裂。在塑性變形時,隨著奧氏體相變形量的增大,誘發的馬氏體相含量也會隨著變形量的增大而增多,殘餘應力也就越高。從而形成惡性循環,在拉伸過程中奧氏體不鏽鋼板材也就越容易出現開裂現象。

其實在奧氏體不鏽鋼板材的拉伸過程中還可以采取下列預防措施:

可以在凹、凸模之間塗上潤滑劑,產生一層具備一定的韌性和延展性的薄膜,這對奧氏體不鏽鋼板材的拉伸效果明顯。

可以采用白口鑄鐵作為壓邊圈磨具,錐形壓邊圈也可以使用,因為白口鑄鐵的存油性能比較好,極易產生潤滑油膜。

把奧氏體不鏽鋼板材的邊緣加工光滑些,不能有微裂缺口,這樣有效避免開裂。